product description

technical parameter

HT-Mn75 manganese agent

1. Purpose:

Adjust the content of manganese in different grades of aluminum alloy to replace the master alloy and reduce the melting temperature.

2. Product features:

1. The element content is 75%

2. The actual yield is greater than 95%

3. Direct investment, easy to use.

3. How to use:

According to the content of alloying elements in the alloy grades produced and the results of the pre-furnace analysis, the required additive amount (quantity of Mn agent) is calculated according to the actual yield of 90%. After the small flame disappears, manual stirring should be appropriately strengthened to make it spread evenly, and according to the actual situation, ensure a certain spread time.

4. Process parameters:

1. Operating temperature: 740-760℃

2. Addition amount (kg) = (alloy element composition (%)-analysis of the element content before the furnace) ÷ actual yield (90%) × alloy element content in the additive (70%) × furnace load (kg)

3. Melting time: 15-30 minutes

5. Packaging and storage:

Product name	model	use	Instructions	Features	Process parameters	specification
HT-Ti	HT-Ti4OB4	Adjust the alloying element composition to replace the aluminum master alloy.	According to the content of alloying elements in the produced alloy grades and the results of the pre-furnace analysis, the actual yield is calculated at 95%. The required additive amount is directly and evenly dispersed into the aluminum bath after the slag is removed, and the small flame disappears After that, manual stirring should be appropriately strengthened to make the diffusion even, and according to the actual situation, ensure a certain diffusion time.	The element content is 75% and the silicon content is 95%. The actual yield is greater than 95%. The actual yield of iron agent is greater than 90%. The shelf life is one year.	Operating temperature: 740℃-760℃. Melting time: 15-30 minutes.	1.500g/piece Density: 3.8-4.2kg/cm3 Si: 2.5g/cm3
HT-Ti	HT-Ti75
HT-Mn	HT-Mn75
HT-Cu	HT-Cu75
HT-Fe	HT-Fe75
HT-Cr	HT-Cr75
HT-Ni	HT-Ni75
HT-Zn	HT-Zn75
HT-Si	HT-Si95